Manufacturers Gtaw Er2594 Welding Wire for Super Duplex

• Customization: Available
• Type: H (Heat Resistant Low Alloy Steel/ Stainless Steel Electrode)
• Material: Stainless Steel
• Model NO.: ER316L/ER310/ER347/ER410/ER2594/ERNICRMO4
• Diameter: 3.2mm
• Length: 400-500mm
• Welding Core Type: Stainless Steel
• Electrode Coating Type: Titanium
• Slag Characteristic: Acidic
• Stainless Steel Welding Rod Type: Chromium Stainless Steel
• Function: Surfacing Electrode, Low Hydrogen Type Electrode, Hardfacing Electrode, High Efficient Iron Powder Electrode, Gravity Electrode, Moisture-Proof Electrode
• Welding Power: DC
• Material Grade: Er316L/Er347/Er410/Er310/Er2594/Ernicrmo4
• Application: Building Material/Industry/Heating Element
• MOQ: 100kgs
• Delivery Time: 15-30 Working Days
• Transport Package: as Your Requirements
• Specification: 1.6-6.0mm
• Trademark: HUICHI
• Origin: China
• HS Code: 8311200000
• Production Capacity: 1000000tons/Year

Product Description

ER2594 Welding Rod Description
Features:
1. Since the weld metal contains about 40% ferrite and combines the comprehensive properties of austenitic and ferritic stainless steel, the pitting resistance index PRE is greater than 40, which has excellent pitting corrosion resistance and stress corrosion resistance;
2. Smooth wire feeding, stable arc, beautiful appearance, less spatter, and excellent welding process performance.
use
It is suitable for welding of 25% bi-directional stainless steel containing chromium in petrochemical and marine engineering industries, such as SUS2507.

Stainless steel electrode should not only meet the general welding process performance and mechanical properties of welding joint, but also ensure that the welding joint can meet the requirements of corrosion resistance. For the coating and core, the following requirements should be considered:
1) Through the transition of various alloy elements between the core and the coating, the weld metal can be made into austenite and ferrite with a certain amount, so as to ensure that the weld metal has good crack resistance and corrosion resistance of corresponding medium.
2) A certain amount of carbide forming elements (such as niobium, molybdenum, titanium, etc.) can be infiltrated into the weld metal through the welding core or coating, which can form stable carbides with carbon to prevent the formation of chromium carbide at the grain boundary.
3) The increase of carbon will cause intergranular corrosion of austenitic stainless steel (or ferritic stainless steel) weld. Therefore, the carbon content in the welding core and coating raw materials should be strictly controlled. It is recommended to use low-carbon or ultra-low-carbon solder core, and use low-carbon or carbon free ferroalloy and metal element as raw materials for coating.
4) The content of sulfur and phosphorus in stainless steel solder core and coating should be strictly controlled to reduce the risk of weld hot crack.
 

	C	Mn	Si	Cr	Ni	Mo	P	S	other
ER316L	0.03	1-2.5	0.65	18-20	11-14	2-3	0.03	0.03	Cu0.75
ER310	0.08-0.15	1-2.5	0.65	25-28	20-22.5	0.75	0.03	0.03	Cu0.75
ER347	0.06	1-2.5	0.65	19-21.5	9-11	0.75	0.03	0.03	Nb 10C-1
ER410	0.12	0.6	0.5	11.5-13.5	0.6	0.75	0.03	0.03	Cu0.75
ER2594	0.03	2.5	1.0	24-27	8-10	2.5-4.5	0.03	0.02	Cu1.5
ERNiCrMo-4	0.02	1	0.08	14.5-16.5	Balance	15-17	0.04	0.03	Fe4-7 W3-4.5